Huntsman IROGRAN ?A89E4372 Thermoplastic Polyurethane Technical Data Sheet |
|||
Huntsman IROGRAN A89E4372適合于制造密封圈、墊片、同步帶、輸送帶、工具帶和汽車行業及電線和電纜、薄膜、片材和型材。 |
|||
Physical Properties物性 |
測試標準 |
數值 |
單位 |
Density密度 |
DIN53479 |
1.19 |
kg/m3 |
Melt Volume Rate(190°C/21.6kg) |
ISO 1133-1 |
4 |
cm3/10min |
Hardness硬度 |
DIN53505 |
89 |
Shore A |
Hardness硬度 |
DIN53505 |
40 |
Shore D |
Mold Shrinkage收縮率 |
ISO 294-4 |
1.1 |
% |
Tensile strength抗拉強度 |
DIN53504 |
50 |
MPa |
Elongation at Break斷裂伸長率 |
DIN53504 |
600 |
% |
100%Modulus伸長模量 |
DIN53504 |
6 |
MPa |
300%Modulus伸長模量 |
DIN53504 |
11.5 |
MPa |
Tear strength撕裂強度 |
DIN53515 |
75 |
KN/m |
Flexural modulus @ 23℃抗彎曲變形模量 |
ASTM D790 |
28.4 |
MPa |
Flexural modulus @ -29℃抗彎曲變形模量 |
ASTM D790 |
96 |
MPa |
Compression Set壓縮變形率23℃×70h |
DIN53517 |
17 |
% |
Compression Set壓縮變形率70℃×24h |
DIN53517 |
38 |
% |
Resilience回彈率 |
DIN52512 |
42 |
% |
Abrasion耐磨性 |
DIN53516 |
28 |
mm3 |
Dew Point露點 |
-30 |
℃ |
|
Glass transition temperature (DSC)玻璃化溫度 |
ASTM D3418 |
-41 |
℃ |
Vicat Softening Point VST/A120維卡軟化點 |
ASTM D1525 |
104 |
℃ |
Melt Range Low熔融溫度(低) |
Huntsman/TMA |
180 |
℃ |
Melt Range High熔融溫度(高) |
Huntsman/TMA |
207 |
℃ |
Melt Range熔融溫度范圍 |
180~200 |
℃ |
聚合物材質 |
聚醚多元醇 |
||||
聚酯多元醇 |
|||||
聚合多元醇 |
|||||
聚氨酯聚合物主要成分 |
CHDI |
PPDI |
NDI |
MDI |
|
IPDI |
HDI |
HMDI |
TDI |
||
聚氨酯聚合物應用領域 |
油缸密封 |
氣缸密封圈 |
防塵密封圈 |
液壓密封圈 |
氣動密封圈 |
破碎錘密封件 |
挖掘機密封圈 |
煤礦用密封件 |
活塞密封圈 |
活塞桿密封 |
|
天然氣密封 |
采油設備密封 |
密封擋圈 |
閥密封 |
O型密封圈 |
|
Y型密封圈 |
V形密封圈 |
KDAS組合密封 |
動密封 |
靜密封 |
|
油封皮碗 |
摩擦輪 |
羅拉roller |
膠輪 |
膠輥 |
|
滾軸 |
導軌耐磨片 |
連接器 |
聯軸器 |
高爾夫球 |