Physical Properties物性 |
測試標準 |
PARKER P6000 |
替代P6000聚氨酯 |
Hardness硬度(邵A) |
DIN53505 |
94 |
94 |
Density密度 |
DIN53479 |
1.2 |
1.2 |
Tensile Strength抗拉強度(MPa) (min.) |
DIN53504 |
58.9 |
55 |
Elongation at Break伸長率(%)(min.) |
DIN53504 |
554 |
500 |
100%Modulus拉伸模量(MPa) (min.) |
DIN53504 |
11 |
12.5 |
300%Modulus拉伸模量(MPa) (min.) |
DIN53504 |
20 |
24.5 |
Tear strength撕裂強度(N/mm) (min.) |
DIN53515 |
94 |
110 |
Compression Set壓縮變形率(%)70℃×70h(25%變形) (max.) |
DIN53517 |
23 |
25 |
Abrasion耐磨性(mm3 ) |
DIN53516 |
— |
30 |
Resilience回彈率(%)(min.) |
DIN52512 |
44 |
35 |
Low temperature shrinkage低溫收縮(℃) |
TR 10 |
-33.1 |
— |
Operating Temperature(Min)最低工作溫度(℃) |
-45 |
-42 |
|
Operating Temperature(Max)最高工作溫度(℃) |
+130 |
+130 |
|
Operating Temp. Range正常工作溫度(℃) |
-35~+110 |
-35~+120 |
|
Glass temperature(Tg,DSC)玻璃化溫度(℃) (max.) |
ISO 11537 |
-35 |
-35 |